Interaction of candidate plasma facing materials with tokamak plasma in COMPASS

The uniformity of the coatings and their thickness was verified before the exposure. After the exposure, no reduction of the thickness was observed, indicating the absence of 'global' erosion. Erosion was observed only in isolated spots, and attributed to unipolar arcing. Slightly larger erosion was found on the steel coatings compared to the tungsten ones. Incorporation of deuterium in a thin surface layer was observed, in dependence on the exposure mode. Additionally, boron enrichment of the long-exposure samples was observed, as a result of the tokamak chamber boronization.