Sintering trials of analogues of americium oxides for radioisotope power systems

The targeted density range of 85-90% was met using both techniques. No ball-milling was required. Cold-pressing-and-sintering CeO2 produced intact discs. Large cracking was prevalent in the SPS discs. Some powders pressed more successfully than others. Powder morphology had a significant effect on the result but it was not possible to fully quantify the effects in this study. The cold-pressed-and-sintered CeO2 discs had comparable Vickers hardness values to a nuclear ceramic (UO2). The hardness values were greater than the spark plasma sintered CeO2 sample. Efforts to SPS near-net shaped pellets using CeO2 and Nd2O3 are reported. A follow on investigation was conducted to assess how the 85-90% T.D. target could be achieved. The aspect ratio impacts the sintering parameters and behaviour. The Vickers hardness of Nd2O3 is reported for the first time and compared to the results of sintered CeO2.