Influence of zeolite precipitation on borosilicate glass alteration under hyperalkaline conditions

This study enables a better understanding of how nucleation-growth of zeolites affects glass dissolution kinetics in hyperalkaline solutions characteristic of cement waters. A 20-oxide borosilicate glass, an inactive surrogate of a typical intermediate level waste glass, was altered in static mode at 50 °C in a hyperalkaline solution rich in Na+, K+ and Ca2+ and at an initial pH50°C of 12.6. Experiments were performed at four glass-surface-area-to-solution-volume (S/V) ratios to investigate various reaction progresses. Two types of glass alteration kinetics were obtained: (i) at low S/V, a sharp alteration resumption occurred after a rate drop regime, (ii) at high S/V, a high dissolution rate was maintained throughout the test duration with a slight progressive slow-down. In all the experiments, zeolites precipitated but the time taken to form stable zeolite nuclei varied dramatically depending on the S/V. Resulting changes in pH affected zeolite composition, morphology, solubility and growth rate. A change in a critical parameter such as S/V affected all the processes controlling glass dissolution.