A novel method to directional solidification of TiAlNb alloys by mixing binary TiAl ingot and Nb wire
چکیده انگلیسی
The method of continuous melting and casting was used in the research to attempt to acquire the ternary directionally solidified Ti-Al-Nb alloy by once casting. It was investigated about microstructure and mechanical properties of the Ti44Al2Nb alloy by changing the temperature gradient. Results show that the lamellar spacing decreased to 1.25 µm, when the temperature gradient increases and the composition is relatively uniform in different regions. The tensile strength, the compressive strength and the fracture toughness of Ti44Al2Nb alloy is 455 MPa, 1770 MPa and 23.5 MPa m1/2 respectively, under the parameters of 50 kW and 0.5 mm/s. The high temperature compressive strength increases, when the strain rate increases and temperature decreases. Because the large strain rate shortens the strain time and piles up dislocations. Another, the low temperature provides the less driving force of dislocation movement. To observe the crack propagation process and the fracture morphology, the fracture mode contains trans-lamellar fracture and interface de-lamination. The method is a feasibility way to prepare the directionally solidified TiAlNb alloy and to add the high-melting-point element into microstructure directly.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: A - Volume 687, 27 February 2017, Pages 181-192
نویسندگان
, , , , , , , ,