Large polaron hopping phenomenon in lanthanum doped strontium titanate
ترجمه فارسی عنوان
پانچ پانکراس پالرن بزرگ در تیتانات استرانسیم دوتایی لانتانیم
موضوعات مرتبط
مهندسی و علوم پایه مهندسی مواد فلزات و آلیاژها
چکیده انگلیسی
A few compositions of La doped strontium titanate, LaxSr1−xTiO3−δ (x = 0.0, 0.1, 0.2, 0.3, and 0.4) were synthesized via solid state reaction route. The XRD patterns of the compositions with x ≤ 0.2 showed single phase whereas for x ≥ 0.3 compositions, secondary phases were observed. The Rietveld refinement of the XRD data for all compositions indicated cubic structure with space group Pm3¯m at room temperature. The SEM micrographs for x = 0.0 showed large grains, whereas the compositions with 0.0 < x ≤ 0.2 showed small grains and for x ≥ 0.3, irregular morphologies with porosity were observed. The conductivity spectra of the investigated systems were described using Jonscher's power law. The scaling behaviour of the systems was understood through Ghosh scaling model. The scaling properties showed that the conduction mechanism is independent of temperature. A systematic study of conduction mechanism of the system revealed that conduction mechanism is changing from small polaron hopping to large polaron hopping as the composition changes from x = 0.0 to x = 0.1. The large polaron hopping has also been confirmed through Modulus spectroscopy and Photoluminiscence analysis in lanthanum substituted samples. Further, the observed change in conduction mechanism was correlated with the hopping polaron size and lattice parameter.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Alloys and Compounds - Volume 704, 15 May 2017, Pages 707-716
نویسندگان
, , , ,