عنوان انگلیسی مقاله ISI
Microstructure thermal stability of nanocrystalline AZ31 magnesium alloy with titanium addition by mechanical milling
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فلزات و آلیاژها
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Microstructure thermal stability of nanocrystalline AZ31 magnesium alloy with titanium addition by mechanical milling Microstructure thermal stability of nanocrystalline AZ31 magnesium alloy with titanium addition by mechanical milling](/preview/png/5460672.png)
چکیده انگلیسی
The nanocrystalline AZ31 magnesium (Mg) alloy with 18 wt% titanium (Ti) addition was isothermally annealed in the temperature range of 300-400 °C for different durations. A study on the thermal stability, including solid solubility evolution, phase transformation, grain growth kinetics and hardness evolution, was carried out. The microstructure evolution at elevated temperatures was investigated by the means of X-ray diffraction (XRD), scanning electron microscope (SEM), transmission electron microscope (TEM) and high angle annular dark field (HAADF). Based on lattice parameters evolution and TEM observation, it was confirmed that the Ti element precipitated from Mg matrix as Ti phase. After the material being annealed at 400 °C for 300min, as to the original Ti particulates, there is no segregation and growth with the average particulate size being approximately 367 nm, meanwhile, magnesium matrix shows limited grain coarsening with the average grain size increasing from 95 nm to 210 nm. In addition, the grain growth kinetics could be well described by the kinetics equation, D7âD07=kt. The activation energy for grain growth was calculated to be 120 kJ/mol, which is about 28 kJ/mol greater than that of pure Mg. Simultaneously, the stability of mechanical property was investigated by microhardness evolution at different annealing temperatures. It was found that after this material being annealed at 400 °C for 300min, the microhardness remained 105HV, which is two times larger than that of the as-cast AZ31 Mg alloy.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Alloys and Compounds - Volume 722, 25 October 2017, Pages 39-47
Journal: Journal of Alloys and Compounds - Volume 722, 25 October 2017, Pages 39-47
نویسندگان
Huan Yu, Haiping Zhou, Yu Sun, Lianxi Hu, Zhipeng Wan,