The influence of Ga doping on structural magnetic and dielectric properties of NiCr0.2Fe1.8O4 spinel ferrite

A series of spinel ferrites NiCr0.2GaxFe1.8−xO4 (x=0.00, 0.002, 0.04, 0.06, 0.08) was prepared by co precipitation technique. The influence of rare earth element Ga ions the structural dielectric and magnetic properties of NiCr0.2Fe1.8O4 ferrites was investigated. The X-ray diffraction confirmed the phase precipitated out was pure spinel phase with few traces of secondary phases. The crystallite size decreases and density increases with the increases of Ga contents. The magnetic moment, saturation magnetization and remanent magnetization increased with addition of Ga ions in spinel ferrite. The dielectric constant is described that it decreases more suddenly at low frequencies as compare at higher frequencies. The decrease in dielectric loss with frequency follows Deby's relaxation phenomena. Both the variation in tan loss and dielectric loss with frequency shows a similar. AC conductivity increases with the increases of frequency which inversely proportional to concentration of Ga3+ ions follows Jonscher law. These Gallium Chromium doped nickel ferrites are very helpful for high frequency switching devices.