Cementitious binders from activated stainless steel refining slag and the effect of alkali solutions
ترجمه فارسی عنوان
اتصال دهنده های سیمان از فولاد ضد زنگ فعال شده از فولاد ضد زنگ و محلول های قلیایی
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
سرباره فولاد ضد زنگ، قلیایی فعال سیمان، استحکام فشاری، تجزیه و تحلیل فاز، تجزیه و تحلیل حرارتی، شستن
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی شیمی
بهداشت و امنیت شیمی
چکیده انگلیسی
With an aim of producing high value cementitious binder, stainless steel refining slag containing a high amount of CaO in γ-dicalcium silicate form was activated with NaOH and Na-silicate as well as KOH and K-silicate solutions, followed by steam curing at 80 °C. Higher levels of alkali-silicate in the activating solution resulted in higher cumulative heat suggesting accelerated reaction kinetics. With respect to compressive strength, higher levels of alkali silicate resulted in higher strength and the mortars with Na activator were found to have higher early strength than the ones with K activator. The long term strength was found to be similar, regardless of the alkali metal. Thermogravimetric, QXRD and FTIR analyses showed an increase in the amount of reaction products (CSH type) over time, further confirming the reactivity of the crystalline slag. Batch leaching results showed lower leaching of heavy metals and metalloids with K activator compared to the Na activator. These results demonstrate that the alkali type and the ratio of hydroxide to silicates have a significant impact on the hydration and mechanical strength development of the stainless steel slag. The above findings can aid in the recycling and valorization of these type of slags which otherwise end up landfilled.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Hazardous Materials - Volume 286, 9 April 2015, Pages 211-219
Journal: Journal of Hazardous Materials - Volume 286, 9 April 2015, Pages 211-219
نویسندگان
Muhammad Salman, Ãzlem Cizer, Yiannis Pontikes, Ruben Snellings, Lucie Vandewalle, Bart Blanpain, Koen Van Balen,