Hydrogen transport behavior of as-cast, cold rolled and annealed Nb40Ti30Co30 alloy membranes
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی شیمی
تصفیه و جداسازی
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Hydrogen transport behavior of as-cast, cold rolled and annealed Nb40Ti30Co30 alloy membranes Hydrogen transport behavior of as-cast, cold rolled and annealed Nb40Ti30Co30 alloy membranes](/preview/png/632283.png)
چکیده انگلیسی
Cold rolling is presently regarded as the most promising route to a large scale fabrication of hydrogen permeable metal membranes. However, complex hydrogen transport behavior appears for such cold rolled membranes due to potential defect formation and recrystallization. Effects of cold rolling and subsequent annealing on hydrogen dissolution, permeation and diffusion in Nb40Ti30Co30 (at%) alloy membranes have been studied. Membranes reduced to 50% thickness by cold rolling exhibit a significantly lower hydrogen permeability than those with as-cast microstructure. This is attributed to the large decrease in both hydrogen solubility and diffusivity as a consequence of rolling. Subsequent annealing of the cold rolled membrane recovers the hydrogen solubility close to that in as-cast state, and significantly increases the diffusivity, leading to an improved permeability. The modified microstructure in the rolled-annealed membrane ensures a high hydrogen permeation flux and a large embrittlement resistance. Typically, a hydrogen flux of ~21 cc H2 cmâ2 minâ1 is obtained for a membrane with 130 µm in thickness at a hydrogen pressure difference of 0.7 MPa at 673 K.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Membrane Science - Volume 514, 15 September 2016, Pages 294-304
Journal: Journal of Membrane Science - Volume 514, 15 September 2016, Pages 294-304
نویسندگان
Xinzhong Li, Dongmei Liu, Xiao Liang, Ruirun Chen, Markus Rettenmayr, Yanqing Su, Jingjie Guo, Hengzhi Fu,