کد مقاله | کد نشریه | سال انتشار | مقاله انگلیسی | نسخه تمام متن |
---|---|---|---|---|
6335104 | 1620240 | 2014 | 14 صفحه PDF | دانلود رایگان |
- Acid sulfate dissolution of clay-rich sediments from inland acid sulfate site in flow-through reactor experiments at pH 1-4.
- Enhanced Al and K release at the higher ionic strength of solutions compared to the lower ionic strength.
- Acid neutralization capacity (ANC) of 1.11 kg H2SO4/tonne clay-rich sediment/day was provided at pH 1, 25 °C.
- ANC provided at 45 °C by the same amount of clay-rich sediment was more than three times higher than the ANC at 25 °C.
Significant amounts of sulfuric acid (H2SO4) rich saline water can be produced by the oxidation of sulfide minerals contained in inland acid sulfate soils (IASS). In the absence of carbonate minerals, the dissolution of phyllosilicate minerals is one of very few processes that can provide long-term acid neutralisation. It is therefore important to understand the acid dissolution behavior of naturally occurring clay minerals from IASS under saline-acidic solutions. The objective of this study was to investigate the dissolution of a natural clay-rich sample under saline-acidic conditions (pH 1-4; ionic strengths = 0.01 and 0.25 M; 25 °C) and over a range of temperatures (25-45 °C; pH 1 and pH 4). The clay-rich sample referred to as Bottle Bend clay (BB clay) used was from an IASS (Bottle Bend lagoon) in south-western New South Wales (Australia) and contained smectite (40%), illite (27%), kaolinite (26%) and quartz (6%). Acid dissolution of the BB clay was initially rapid, as indicated by the fast release of cations (Si, Al, K, Fe, Mg). Relatively higher Al (pH 4) and K (pH 2-4) release was obtained from BB clay dissolution in higher ionic strength solutions compared to the lower ionic strength solutions. The steady state dissolution rate (as determined from Si, Al and Fe release rates; RSi, RAl, RFe) increased with decreasing solution pH and increasing temperature. For example, the highest log RSi value was obtained at pH 1 and 45 °C (â9.07 mol gâ1 sâ1), while the lowest log RSi value was obtained at pH 4 and 25 °C (â11.20 mol gâ1 sâ1). A comparison of these results with pure mineral dissolution rates from the literature suggests that the BB clay dissolved at a much faster rate compared to the pure mineral samples. Apparent activation energies calculated for the clay sample varied over the range 76.6 kJ molâ1 (pH 1) to 37.7 kJ molâ1 (pH 4) which compare very well with the activation energy values for acidic dissolution of monomineralic samples e.g. montmorillonite from previous studies. The acid neutralisation capacity (ANC) of the clay sample was calculated from the release of all structural cations except Si (i.e. Al, Fe, K, Mg). According to these calculations an ANC of 1.11 kg H2SO4/tonne clay/day was provided by clay dissolution at pH 1 (I = 0.25 M, 25 °C) compared to an ANC of 0.21 kg H2SO4/tonne clay/day at pH 4 (I = 0.25 M, 25 °C). The highest ANC of 6.91 kg H2SO4/tonne clay/day was provided by clay dissolution at pH 1 and at 45 °C (I = 0.25 M), which is more than three times higher than the ANC provided under the similar solution conditions at 25 °C. In wetlands with little solid phase buffering available apart from clay minerals, it is imperative to consider the potential ANC provided by the dissolution of abundantly occurring phyllosilicate minerals in devising rehabilitation schemes.
Journal: Applied Geochemistry - Volume 51, December 2014, Pages 170-183