The high-temperature, water-gas shift reaction was conducted in 100 wt%Pd and 80 wt%Pd–20 wt%Cu (Pd80 wt%Cu) shell-and-tube membrane reactors at 1173 K with a 241 kPa (35 psig) trans-membrane pressure differential in the absence of heterogeneous catalyst particles. The tube bundle consisted of four parallel 15.25 cm long, 3.175 mm OD Pd-based tubes with a wall thickness of 125 μm. The modest catalytic activity of the Pd-based membrane surface for the forward WGSR, the high rate of hydrogen extraction through the Pd-based membranes, and the long residence times (1–5 s) resulted in a dramatic shift in carbon monoxide conversions of 93% at 1173 K and a 1.5:1 steam-to-carbon monoxide feed ratio—a value well above the equilibrium value of ∼54% associated with a conventional (non-membrane) reactor. Carbon monoxide conversions decreased from 93% to 66% and hydrogen recovery from 90% to 85% at a residence time of 5 s when the Pd was replaced with Pd80 wt%Cu, due to the lower permeance of the Pd80 wt%Cu alloy. SEM-EDS analysis of the membrane tubes suggested that the water-gas shift environment caused pinhole formation in the retentate surfaces of the Pd and Pd80 wt%Cu after approximately 8 days of operation.
Journal: Journal of Membrane Science - Volume 298, Issues 1–2, 20 July 2007, Pages 14–23