عنوان انگلیسی مقاله ISI
Swelling-agent-free synthesis of rice husk derived silica materials with large mesopores for efficient CO2 capture
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی شیمی
مهندسی شیمی (عمومی)
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Swelling-agent-free synthesis of rice husk derived silica materials with large mesopores for efficient CO2 capture Swelling-agent-free synthesis of rice husk derived silica materials with large mesopores for efficient CO2 capture](/preview/png/6586281.png)
چکیده انگلیسی
Swelling-agent-free synthesis of silica materials with large mesopores were developed using silicate from rice husk ash (RHA) as an alternative silica precursor in this study. Unlike the conventional methods for preparing large-pore silica materials in which toxic and expensive additives were employed as swelling agents, the obtained silica materials with large mesopores could be facilely prepared via a simple temperature-controlled approach without adding pore expanders. The fusion and hydrothermal temperature effects on the structural properties of obtained mesoporous silicas were investigated by the XRD, nitrogen adsorption-desorption, SEM and TEM analyses. The obtained mesoporous MS-400(25), which was fabricated using rice husk fused at 400 °C and treated with sodium hydroxide at 25 °C, exhibited bimodal meso-porosities (2.7 and 24 nm) and large pore volume (1.92 cm3/g). The bi-porosities mainly originated from the intra-particle mesostructure within silica particles and the inter-particle porosity between the aggregated nano-sized silica particles, respectively. The synthesized silicas were applied as the supports of adsorbents for CO2 capture. The adsorption tests clearly revealed that the tetraethylenepentamine (TEPA) impregnated MS-400(25) material could achieve CO2 adsorption capacity of 173 mg/g under 10% CO2 at 75 °C, which was the best sorbents among all samples due to its relatively large pore volume.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Chemical Engineering Journal - Volume 251, 1 September 2014, Pages 1-9
Journal: Chemical Engineering Journal - Volume 251, 1 September 2014, Pages 1-9
نویسندگان
Wanting Zeng, Hsunling Bai,