Strength properties and molecular composition of epoxy-modified mortars
ترجمه فارسی عنوان
خواص مقاومت و ترکیب مولکولی ملات ها اصلاح شده با اپوکسی
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
رزین اپوکسی، استحکام، توسعه قدرت، ملات اصلاح شده اپوکسی،
موضوعات مرتبط
مهندسی و علوم پایه
سایر رشته های مهندسی
مهندسی عمران و سازه
چکیده انگلیسی
Even without hardener, epoxy resin is able to harden in the presence of hydroxyl ions produced during cement hydration process. In this study commercially available Bisphenol A-type epoxy resin without hardener was used as a polymeric admixture to prepare epoxy-modified mortars, whose properties and chemical composition were then investigated. The mortars were prepared with a mass ratio of 1:3 (cement:fine aggregate), water-to-cement ratio (W/C) of 0.48, and epoxy content of 5%, 10%, 15% and 20% of cement. The specimens were subjected to dry and wet-dry curing. Workability, setting time, compressive strength, flexural strength, and tensile splitting strength tests were conducted. A Fourier transformation infrared spectroscopy test was also administered to determine the molecular composition and structure of mortars. Results showed an inverse relationship between workability and setting time of mortars versus epoxy content. The compressive, flexural, and tensile splitting strengths of epoxy-modified mortars were noted to be the highest for mortars containing 10% epoxy in wet-dry curing. A significant improvement in strength development of mortars without hardener had been achieved through dry curing due to gradual hardening of epoxy resin with hydrated cement.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Construction and Building Materials - Volume 94, 30 September 2015, Pages 315-322
Journal: Construction and Building Materials - Volume 94, 30 September 2015, Pages 315-322
نویسندگان
Nur Farhayu Ariffin, Mohd Warid Hussin, Abdul Rahman Mohd Sam, Muhammad Aamer Rafique Bhutta, Nur Hafizah Abd. Khalid, Jahangir Mirza,