Effect of sequential Fe2+ − C+ implantation on deuterium retention in W
موضوعات مرتبط
مهندسی و علوم پایه مهندسی انرژی مهندسی انرژی و فناوری های برق
پیش نمایش صفحه اول مقاله
Effect of sequential Fe2+ − C+ implantation on deuterium retention in W
چکیده انگلیسی
Deuterium (D) retention behavior for the sequential 6 MeV iron (Fe) and 10 keV carbon (C) implanted tungsten (W) were evaluated by thermal desorption spectroscopy (TDS) and β-ray-induced X-ray spectroscopy (BIXS) to understand the synergetic effect of defect formation and C existence on D retention behavior for W under various damage distribution profiles. The experimental results indicated that retention of D trapped by dislocation loops was controlled by 10 keV C+ implantation. The D retention was reduced in the sequential Fe2+ − C+ implanted W with higher C+ fluence in comparison to that with lower C+ fluence due to the formation of C-W layer which suppressed D diffusion toward the bulk and dense defects at the surface which reduce effective D diffusion coefficient. On the other hand, the amount of D trapped by the defects in the deeper region than C+ implantation region (50 nm) was increased due to the formation of dense defects by 6 MeV Fe2+ implantation within the depth of 1.5 μm.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Fusion Engineering and Design - Volume 124, November 2017, Pages 231-234
نویسندگان
, , , , , , , , , , ,