• Controlled sized PAA-b-PBA block copolymers were adsorbed on polymer particles.
• Their effect on polymer interdiffusion (FRET) and mechanical properties was studied.
• Longer acidic lengths led to worse interdiffusion and mechanical properties.
• Higher annealing temperatures and using NH4OH instead of NaOH produced better films.
The effect of the acidic hairy layer length on the interdiffusion of polymer between particles and as a consequence on the mechanical properties of the films produced from waterborne coatings has been studied. In order to isolate this effect, latexes with the same particle diameter and molecular weight but stabilized with poly(acrylic acid)-block-poly(butyl acrylate) (PAA-b-PBA) block copolymers of controlled and different lengths were prepared. Tensile strength measurements showed at the macroscopic level that the presence of AA chains in the particle surface reduced the mechanical properties of the films dried at room temperature, being its effect worse the longer the AA chain length. Higher annealing temperatures erased the negative effect of the acidic hairy layer on mechanical properties. The neutralization with NaOH instead of with NH4OH also led to worse mechanical properties. These macroscopic results were supported by Fluorescence Resonance Energy Transfer (FRET) experiments that showed that at the microscopic level, the extent of interdiffusion occurred slower when the AA chains in the particles surface increased, the annealing temperature was lower and when NaOH was used as neutralizing agent instead of NH4OH.
Figure optionsDownload as PowerPoint slide
Journal: Progress in Organic Coatings - Volume 88, November 2015, Pages 137–143