![عکس صفحه اول مقاله: Deposition of hybrid 3-GPTMS's film on AA2024-T3: Dependence of film morphology and protectiveness performance on coating conditions Deposition of hybrid 3-GPTMS's film on AA2024-T3: Dependence of film morphology and protectiveness performance on coating conditions](/preview/png/692741.png)
This paper describes the elaboration of 3-glycidoxypropyltrimethoxysilane (3-GPTMS) films onto AA2024-T3 aluminum alloy for corrosion protection.The dependence of sol–gel morphology on both precipitation under cathodic polarization and nitrate incorporation was investigated via scanning electron microscopy (SEM).Once added into silanization solution, sodium nitrate promoted the reaction of silane condensation and enhanced the film compactness.Electrochemical impedance spectroscopy results (EIS) indicated that doping silane film with NaNO3 ameliorated its barrier property and protectiveness. Silane films applied onto AA2024-T3 surface by using potentiostatic method, exhibited obviously higher corrosion resistance than those obtained by conventional “dip-coating” method. The resistance of coating is accentuated when not very negative potential was applied.
► 3-glycidoxypropyltrimethoxysilane films were elaborated onto AA2024-T3 surface from solution containing or not NO3− ions.
► Films are prepared by both dip-coating and precipitation under cathodic polarization techniques.
► Prepared using potentiostatic method and in presence of NO3−, coating exhibit higher resistance in chloride media.
Journal: Progress in Organic Coatings - Volume 73, Issues 2–3, February–March 2012, Pages 264–271