Hot filament chemical vapour deposition and wear resistance of diamond films on WC-Co substrates coated using PVD-arc deposition technique

Different Cr- and Ti-base films were deposited using PVD-arc deposition onto WC-Co substrates, and multilayered coatings were obtained from the superimposition of diamond coatings, deposited on the PVD interlayer using hot filament chemical vapour deposition (HFCVD). The behaviour of PVD-arc deposited CrN and CrC interlayers between diamond and WC-Co substrates was studied and compared to TiN, TiC, and Ti(C,N) interlayers. Tribological tests with alternative sliding motion were carried out to check the multilayer (PVD + diamond) film adhesion on WC-Co substrate. Multilayer films obtained using PVD arc, characterised by large surface droplets, demonstrated good wear resistance, while diamond deposited on smooth PVD TiN films was not adherent. Multilayered Ti(C,N) + diamond film samples generally showed poor wear resistance.Diamond adhesion on Cr-based PVD coatings deposited on WC-Co substrate was good. In particular, CrN interlayers improved diamond film properties and 6 μm-thick diamond films deposited on CrN showed excellent wear behaviour characterised by the absence of measurable wear volume after sling tests. Good diamond adhesion on Cr-based PVD films has been attributed to chromium carbide formation on PVD film surfaces during the CVD process.