Hydrogen-microvoid interactions at continuum scale
ترجمه فارسی عنوان
تعاملات هیدروژن-میکرووویو در مقیاس پیوندی
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
تعامل هیدروژن و میکرووویید، هیدروژن پلاستیکی موضعی را افزایش می دهد، شکستگی گردن داخلی شکستن داخلی برشی، شکست لوسی،
موضوعات مرتبط
مهندسی و علوم پایه
شیمی
الکتروشیمی
چکیده انگلیسی
Experimentally, it has been shown that hydrogen can either enhance the internal necking failure or induce internal shearing failure of microvoids. In this study, the numerical investigation of hydrogen-microvoid interactions under the framework of hydrogen enhanced localized plasticity mechanism reveals that the actual effect of hydrogen depends on the stress state as well as on the hydrogen trapping effect. Hydrogen enhanced internal necking failure is observed over the entire stress space at a low level of trapping effect. While such failure is still observed in the high triaxiality regime at a high level of trapping effect, hydrogen induced internal shearing failure is observed in the low triaxiality regime. A hydrogen induced internal shearing failure criterion is proposed, and the failure loci corresponding to the low and high levels of trapping effect are constructed. The hydrogen induced internal shearing failure locus is found to be approximately independent of stress triaxiality while the hydrogen enhanced internal necking failure locus maintains similar triaxiality dependency as in the absence of hydrogen. The loss of ductility, in terms of reduction in failure strain and dimple size, is more pronounced in the case of hydrogen induced internal shearing failure. Subsequent study of the Lode effect reveals that plane strain tension is the most critical case for hydrogen induced internal shearing failure while axisymmetric tension is the most critical for hydrogen enhanced internal necking failure.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: International Journal of Hydrogen Energy - Volume 43, Issue 21, 24 May 2018, Pages 10104-10128
Journal: International Journal of Hydrogen Energy - Volume 43, Issue 21, 24 May 2018, Pages 10104-10128
نویسندگان
Haiyang Yu, Jim Stian Olsen, Jianying He, Zhiliang Zhang,