A study on optimal pore range for high pressure hydrogen storage behaviors by porous hard carbon materials prepared from a polymeric precursor
ترجمه فارسی عنوان
یک مطالعه برای محدوده منافذ مطلوب برای رفتار ذخیره سازی هیدرولیکی فشار بالا توسط مواد کربن متخلخل تهیه شده از پیش ماده پلیمری
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
کربن سخت فعال شده ذخیره سازی هیدروژن، ساختار پوسته، فعال سازی بخار،
موضوعات مرتبط
مهندسی و علوم پایه
شیمی
الکتروشیمی
چکیده انگلیسی
In this study, activated polymer-based hard carbons were prepared using various steam activation conditions in order to enhance their hydrogen storage ability. The structural characteristics of the activated carbons were observed by X-ray diffraction and Raman spectroscopy. The N2 adsorption isotherm characteristics at 77Â K were confirmed by Brunauer-Emmett-Teller, Barrett-Joyner-Halenda and non-local density functional theory equations. The hydrogen storage behaviours of the activated carbons at 298Â K and 10Â MPa were studied using a Pressure-Composition-Temperature apparatus. From the results, specific surface areas and total pore volume of the activated carbons were determined to be 1680-2320Â m2/g and 0.78-1.39Â cm3/g, respectively. It was also observed that various pore size distributions were found to be dependent on the functions of activation time. In the observed result, the hydrogen adsorption of APHS-9-4 increased about 30% more than that of as-prepared hard carbon. This indicates that hydrogen storage capacity could be a function not only of specific surface area or total pore volume, but also of micropore volume fraction in the range of 0.63-0.78Â nm of adsorbents.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: International Journal of Hydrogen Energy - Volume 43, Issue 11, 15 March 2018, Pages 5894-5902
Journal: International Journal of Hydrogen Energy - Volume 43, Issue 11, 15 March 2018, Pages 5894-5902
نویسندگان
Hye-Min Lee, Young-Jung Heo, Kay-Hyeok An, Sang-Chul Jung, Dong Chul Chung, Soo-Jin Park, Byung-Joo Kim,