Interaction of La0.58Sr0.40Co0.20Fe0.80O3âδ cathode with volatile Cr in a stack test - Scanning electron microscopy and transmission electron microscopy investigations
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
شیمی
الکتروشیمی
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
Anode-supported solid oxide fuel cells with special thin-film yttria-stabilized zirconia electrolytes made by sol-gel technology were operated in a short stack sequentially for about 1300 h at temperatures of 700 °C and subsequently for 1200 h at 600 °C, respectively. The stack was operated galvanostatically at a constant current density of 500 mA cmâ2. After operation, the stack was dismantled and the cells were analyzed with respect to Cr interaction with the LSCF cathode. Chemical analysis revealed typical overall Cr amounts of several tenths μg cmâ2 cathode area depending on the operation time. SEM cross sections showed less SrCrO4 formation at the typical sites for LSCF (top side of cathode) but there was evidence of chromate formation at the border between the cathode and barrier (electrolyte) layer. This location of foreign phase formation was unexpected. Additional TEM characterizations were therefore conducted. The TEM investigation verified the presence of Cr-containing crystals and revealed pore formation in the barrier layer. The formation of SrCrO4 at this borderline and pore formation were found for the first time after SOFC stack operation.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Power Sources - Volume 254, 15 May 2014, Pages 148-152
Journal: Journal of Power Sources - Volume 254, 15 May 2014, Pages 148-152
نویسندگان
Norbert H. Menzler, Doris Sebold, Egbert Wessel,