Fabrication of (PPC/NCC)/PVA composites with inner-outer double constrained structure and improved glass transition temperature

Improving glass transition temperature (Tg) and mechanical property of the environment-friendly poly(propylene carbonate) via intermacromolecular complexation through hydrogen bonding is attractive and of great importance. A novel and effective strategy to prepare (polypropylene carbonate/nanocrystalline cellulose)/polyvinyl alcohol ((PPC/NCC)/PVA) composites with inner-outer double constrained structure was reported in this work. Outside the PPC phase, PVA, as a strong skeleton at microscale, could constrain the movement of PPC molecular chains by forming hydrogen bonding with PPC at the interface of PPC and PVA phases; inside the PPC phase, the rod-like NCC could restrain the flexible molecular chains of PPC at nanoscale by forming multi-hydrogen bonding with PPC. Under the synergistic effect of this novel inner-outer double constrained structure, Tg, mechanical properties and thermal stability of (PPC/NCC)/PVA composite were significantly increased, e.g. Tg of the composite researched the maximum value of 49.6 °C, respectively 15.6 °C, 5.7 °C and 4.2 °C higher than that of PPC, PPC/NCC and PPC/PVA composite.