عنوان انگلیسی مقاله ISI
Effect of coating thickness and annealing temperature on ZrN coating failure of U-Mo particles under heat treatment
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی انرژی
انرژی هسته ای و مهندسی
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Effect of coating thickness and annealing temperature on ZrN coating failure of U-Mo particles under heat treatment Effect of coating thickness and annealing temperature on ZrN coating failure of U-Mo particles under heat treatment](/preview/png/7963152.png)
چکیده انگلیسی
Zirconium nitride (ZrN) coating is used as a diffusion barrier layer on U-Mo powder surfaces to suppress interdiffusion layer formation. However, it has been reported that the structural integrity of the coating did not remain intact after fuel plate fabrication process. To assess the coating integrity during the fabrication process at high temperature, parametric studies were performed with different coating layer thicknesses and annealing temperatures for ZrN-coated U-7w.t.%Mo particles. The microstructure of the annealed samples was analyzed by using scanning emission microscopy (SEM) and X-ray diffraction. Finite element simulations were performed whether mechanical failure of the coating layer occurs under given annealing temperatures. The simulation results showed the effect of coating layer thickness and annealing temperature on the coating fracture. It was found that tensile hoop stress became larger to cause fracturing over the coating layers as the annealing temperature increased, which was consistent with the results of SEM analysis. By comparing experimental results with simulation results, the thresholds of coating layer thickness and annealing temperature for crack initiation was primarily determined by the U-7Mo particle size.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Nuclear Materials - Volume 507, 15 August 2018, Pages 347-359
Journal: Journal of Nuclear Materials - Volume 507, 15 August 2018, Pages 347-359
نویسندگان
Ji-Hyeon Kim, Gwan Yoon Jeong, Sunghwan Kim, Yong Jin Jeong, Dong-Seong Sohn,