Citrate gel-combustion synthesis and sintering of nanocrystalline ThO2 powders

A systematic study of the influence of citric acid to nitrate mole (R) ratio (R = 0 to 0.50) on the citrate gel-combustion synthesis of nanocrystalline (nc) ThO2 in bulk quantities (30 g) by using citrate gel-combustion was carried out. The nc-ThO2 powders were characterized for their bulk density, size distribution of particles, specific surface area, carbon residue and X-ray crystallite size. All these powders were compacted at pressures varying from 60 to 353 MPa and sintered by using the “two-step sintering” method. Powders prepared from a mixture with an “R” value of 0.125 compacted at 243 MPa yielded a maximum sintered density of 98.8 ± 0.3% T.D. For nc-ThO2, this is the highest sintered density reported so far. The microstructural investigations on nc-ThO2 powders were carried out by using both scanning electron microscopy (SEM) and transmission electron microscopy (TEM). SEM images of the sintered thoria monoliths revealed faceted grains with well defined grain boundaries. Shrinkage anisotropy factor (α) revealed that the compacts prepared from the powders obtained from starting mixtures with R values of 0.125-0.50 had undergone uniform sintering (near isotropic shrinkage).