Chemical potential of oxygen in (U, Pu) mixed oxide with Pu/(U+Pu)Â =Â 0.46

Chemical potential of oxygen in (U,Pu) mixed oxide with Pu/(U + Pu) = 0.46 was measured for the first time using H2/H2O gas equilibration combined with solid electrolyte EMF technique at 1073, 1273 and 1473 K covering an oxygen potential range of −525 to −325 kJ mol−1. The effect of oxygen potential on the oxygen to metal ratio was determined. Increase in oxygen potential increases the O/M. In this study the minimum O/M obtained was 1.985 below which reduction was not possible. Partial molar enthalpy ΔH¯O2 and entropy ΔS¯O2 of oxygen were calculated from the oxygen potential data. The values of −752.36 kJ mol−1 and 0.25 kJ mol−1 were obtained for ΔH¯O2 and ΔS¯O2 respectively.