Effect of pre-strain on susceptibility of Indian Reduced Activation Ferritic Martensitic Steel to hydrogen embrittlement

The role of pre-strain on hydrogen embrittlement susceptibility of Indian Reduced Activation Ferritic Martensitic Steel was investigated using constant nominal strain-rate tension test. The samples were pre-strained to different levels of plastic strain and their mechanical behavior and mode of fracture under the influence of hydrogen was studied. The effect of plastic pre-strain in the range of 0.5-2% on the ductility of the samples was prominent. Compared to samples without any pre-straining, effect of hydrogen was more pronounced on pre-strained samples. Prior deformation reduced the material ductility under the influence of hydrogen. Up to 35% reduction in the total strain was observed under the influence of hydrogen in pre-strained samples. Hydrogen charging resulted in increased occurrence of brittle zones on the fracture surface. Hydrogen Enhanced Decohesion (HEDE) was found to be the dominant mechanism of fracture.