Over-ageing of an Al-Mg-Si alloy with silicon excess
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
دانش مواد (عمومی)
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
The over-ageing of an Al-Mg-Si alloy with Silicon excess was investigated using global thermoelectric power (TEP) and hardness measurements combined with local techniques (Transmission Electron Microscopy (TEM) and Atom Probe Tomography (APT)), in order to highlight how the peak-aged microstructure obtained by a T6 treatment evolves in use conditions at temperatures between 100â¯Â°C and 350â¯Â°C, leading to a progressive loss of mechanical strength. First, TEP was found to be relevant to study the over-ageing kinetics of the alloy due to its perfect correlation with hardness and its sensitivity to the microstructural changes occurring after peak hardness. Then, APT and TEM observations clearly showed that over-ageing is due to the progressive replacement of the βⳠphase by a succession of different types of semi-coherent phases (firstly, of Type B and then of Type A and Type C) and by an extensive precipitation of pure silicon particles. At the highest temperature (Tâ¯=â¯350â¯Â°C), it was highlighted that the influence of manganese cannot be neglected. From these studies, an experimental Isothermal Transformation Curve could be proposed in the investigated temperature range. Lastly, the decrease in mechanical strength taking place during isothermal and non-isothermal ageing from a T6 state was experimentally characterised and successfully analysed using the JMAK formalism.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: A - Volume 730, 11 July 2018, Pages 92-105
Journal: Materials Science and Engineering: A - Volume 730, 11 July 2018, Pages 92-105
نویسندگان
G. Meyruey, V. Massardier, W. Lefebvre, M. Perez,