Microstructural study in a Fe-Ni-base superalloy during creep-rupture at intermediate temperature
موضوعات مرتبط
مهندسی و علوم پایه مهندسی مواد دانش مواد (عمومی)
پیش نمایش صفحه اول مقاله
Microstructural study in a Fe-Ni-base superalloy during creep-rupture at intermediate temperature
چکیده انگلیسی
Creep-rupture behavior of a Fe-Ni-base alloy crept under various conditions has been studied using Electron Backscatter Diffraction (EBSD) and Transmission electron microscopy (TEM). The results indicate that grain orientation did not change after the alloy crept at 700 °C/300 MPa and changed greatly crept at 700 °C/200 MPa. The recrystallization texture near rupture-fracture surface was observed after the alloy crept at 750 °C/150 MPa. A better creep performance was found in the samples with the occurrence of grain rotation dependence of the microstructure and the grain store energy.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials Science and Engineering: A - Volume 639, 15 July 2015, Pages 15-20
نویسندگان
, , , , , , ,