Thermal stability of microstructures induced by laser shock peening in TC17 titanium alloy
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فلزات و آلیاژها
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
The thermal stability of microstructures induced by laser shock peening (LSP) in TC17 titanium alloy (Ti-5Al-2Sn-2Zr-4Mo-4Cr) was investigated by comparing the microstructural characteristics and mechanical properties, which were characterized by transmission electron microscopy (TEM) and Vickers hardness tests of LSPed and subsequently annealed samples. The LSPed TC17 titanium alloy samples were annealed at 573, 623, 673, and 723â¯K for 1 h. Comparison of the gradient microstructures studied at different depths of the LSPed and LSP+573 K/1â¯h and LSP+673 K/1â¯h annealed specimens indicated that the dislocation density markedly decreased and the dislocation cells became clearer in the 573â¯K/1â¯h annealed specimen while there were no great changes in deformation twin density and the average grain size at the surface did not change greatly. After annealing at 673â¯K for 1â¯h, the dislocation density and deformation twins density both decreased greatly at different depths and the average grain size at the surface increased compared to the LSPed and 573â¯K/1â¯h annealed specimens. The average grain sizes in the top surface layers of the LSPed, 573â¯K/1â¯h, 623â¯K/1â¯h, 673â¯K/1â¯h and 723â¯K/1â¯h annealed samples were 396â¯nm, 422â¯nm, 493â¯nm, 1.04â¯Î¼m, and 2.46â¯Î¼m, respectively. The critical temperature at which the microstructures of the LSPed TC17 titanium alloy changed significantly was 673â¯K; the fine grains at the top surface started abnormal growth when the annealing temperature exceeded that value. The hardness values decreased significantly when the annealing temperature reached 673â¯K. It can be concluded that 673â¯K was the critical temperature below which the microstructures induced by LSP were thermally stable in the TC17 titanium alloy.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Alloys and Compounds - Volume 767, 30 October 2018, Pages 253-258
Journal: Journal of Alloys and Compounds - Volume 767, 30 October 2018, Pages 253-258
نویسندگان
Yang Yang, Kai Zhou, Hua Zhang, Haibo Hu, Hongchao Qiao,