Microstructure evolution and mechanical properties of linear friction welded Ti2AlNb alloy
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فلزات و آلیاژها
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
A Ti2AlNb-based alloy was welded by linear friction welding (LFW). The microstructure and mechanical properties of the LFWed joint were investigated. The results indicate that a defect-free joint can be obtained using LFW. The weld zone of the welded joint is composed of B2 phase and a few residual O and α2 phases, and it features primarily low angle grain boundaries. In thermo-mechanically affected zone, most O phase has gradually turned into B2 phase and the α2 phase has changed into a small spherical microstructure. With increasing the distance from the weld zone to the base metal, more coarse and needle-shaped O phase could be found while α2 phase almost remain unchanged. The microhardness presents a total decrease by about 80HV from the base metal to the weld interface. The average tensile strength of the joint at room temperature is 1136 MPa, which is basically comparable to that of the base metal. And the tensile elongation of the joint achieves 76% of the base metal.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Alloys and Compounds - Volume 646, 15 October 2015, Pages 490-496
Journal: Journal of Alloys and Compounds - Volume 646, 15 October 2015, Pages 490-496
نویسندگان
X. Chen, F.Q. Xie, T.J. Ma, W.Y. Li, X.Q. Wu,