Time and temperature regime of continuous grain coarsening in an ECAP-processed Al(0.1Â wt.% Sc) alloy
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فلزات و آلیاژها
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Time and temperature regime of continuous grain coarsening in an ECAP-processed Al(0.1Â wt.% Sc) alloy Time and temperature regime of continuous grain coarsening in an ECAP-processed Al(0.1Â wt.% Sc) alloy](/preview/png/8003559.png)
چکیده انگلیسی
An equiaxed, submicron grain size distribution was generated in an Al(0.1 wt.% Sc) alloy by processing through equal channel angular pressing followed by a low temperature pre-ageing heat treatment. The alloy was subsequently annealed for various times at 300, 350, 400 and 450 °C for investigating the thermal stability of the deformation microstructure. It was found that up to 400 °C, the submicron grain structure coarsens slowly and uniformly by a process of continuous recrystallization. Within this temperature range, the uniform dispersion of nano-sized Al3Sc particles generated by the pre-ageing treatment substantially hinders grain coarsening by Zener pinning of the (sub)grain boundaries. At the higher annealing temperature of 450 °C, certain grains were found to grow discontinuously thereby generating a mixed microstructure consisting of both fine and coarse grains. The data in this study was combined with recent data for a higher solute Al(0.3 wt.% Sc) alloy for furthering our understanding of the time and temperature range in which this family of alloys is resistant to rapid, discontinuous grain coarsening (recrystallization).
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Alloys and Compounds - Volume 527, 25 June 2012, Pages 145-151
Journal: Journal of Alloys and Compounds - Volume 527, 25 June 2012, Pages 145-151
نویسندگان
A. Bommareddy, M.Z. Quadir, M. Ferry,