Influence of ceramic top coat and thermally grown oxide microstructures of air plasma sprayed Sm2SrAl2O7 thermal barrier coatings on the electrochemical impedance behavior

The impedance responses of SSA top coat, TGO, and TGO-bond coat interface were reduced drastically after oxidation at 1100 °C for 10 h pre-oxidized specimen as compared to 20 and 30 h due to the compositional change of pure α-Al2O3 based TGO into more conductive NiCr2O4. The lowest diffusion coefficient, DCr3+ in the NiO lattice which reduced the formation of metal ion vacancies at the TGO-top coat interface caused to exhibit higher TGO resistance for 20 h pre-oxidized specimens over 10 and 30 h after oxidation at 1100 °C.