Structure, mechanical and friction behavior of laminar Ti-incorporated Al2O3 thermal control films deposited on polyethylene terephthalate flexible substrates
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سطوح، پوششها و فیلمها
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Structure, mechanical and friction behavior of laminar Ti-incorporated Al2O3 thermal control films deposited on polyethylene terephthalate flexible substrates Structure, mechanical and friction behavior of laminar Ti-incorporated Al2O3 thermal control films deposited on polyethylene terephthalate flexible substrates](/preview/png/8044161.png)
چکیده انگلیسی
Nano-multilayered Ti-Al2O3 films with different Ti layer thicknesses were fabricated on polyethylene terephthalate flexible substrates by roll to roll magnetron sputtering. The morphologies and structure of the multilayer films were investigated by scanning electron microscopy and X-ray diffraction. Multilayer films show dense and coherent epitaxial growth due to the mutual growth-promoting effect. Bruker tester, nano-indenter and tribometer were used to examine the adhesion strength, mechanical and tribological properties of Ti-Al2O3 multilayer films. Results indicate that multilayer films can be deformed together with PET substrate and withstand the larger strain without cracking. The mean value of adhesion strength of the multilayer films obtained from the scratch tests are in the range of 14.5-16.3â¯mN. The multilayer films with Ti layer thickness of 8.3â¯nm have the highest hardness of 21.3â¯GPa, lowest friction coefficient of 0.32 and lowest wear rate of 2.46Ã10â6 mm3/Nm.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Vacuum - Volume 154, August 2018, Pages 244-249
Journal: Vacuum - Volume 154, August 2018, Pages 244-249
نویسندگان
Feng Xu, Dongmei Gong, Wenchao Shi,