Corrosion of C110 carbon steel in high-pressure aqueous environment with mixed hydrocarbon and CO2 gas
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
علوم زمین و سیارات
زمین شناسی اقتصادی
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
When CPPR was varied from 0 to 100%, similar corrosion rate trends were observed at 41.37 and 62.05Â MPa. Corrosion rate increased to a maximum value and subsequently decreased as the CPPR was increased to 100%. A dense and compact corrosion product was formed at 41.37Â MPa and 100% CPPR. To detect presence of localized corrosion, total reduction in Load Carrying Capacity (LCC) and reduction in LCC due to uniform corrosion were determined and compared. Results show no mechanical property degradation after exposure indicating absence of localized corrosion. The total reduction was slightly higher than the reduction due to uniform corrosion. One possible explanation for this observation could be minor variation of corroded specimen thickness, which resulted in underestimation of LCC reduction due to uniform corrosion.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Petroleum Science and Engineering - Volume 146, October 2016, Pages 777-787
Journal: Journal of Petroleum Science and Engineering - Volume 146, October 2016, Pages 777-787
نویسندگان
Rida Elgaddafi, Ramadan Ahmed, Shokrollah Hassani, Subhash Shah, Samuel O. Osisanya,