Comparative study of nano-sized particles CoFe2O4 effects on superconducting properties of Y-123 and Y-358

The effects of nano-sized CoFe2O4 particles (10 nm) addition on the structural and the normal state resistivity of YBa2Cu3O7 (noted Y-123) and Y3Ba5Cu8O18 (noted Y-358) polycrystalline were systematically studied. Samples were synthesized in oxygen atmosphere using a standard solid state reaction technique by adding CoFe2O4 up to 2 wt%. Phases, microstructure and superconductivity have been systematically investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM) and electrical measurements ρ(T). XRD results reveal that the lattice parameters change for both Y-123 and Y-358 phases. SEM observations reveal that the grain size is reduced with increasing the content of CoFe2O4. The measurements for the resistivity dependence of temperature show that the depression in superconducting temperature is more pronounced for CoFe2O4 addition in Y-358 compound than in Y-123 one. These results may be attributed to the existence of much more disorder due to a greater number of Cu sites to be substituted by Fe and Co in Y-358 compared to Y-123.