Green Nanotechnology for Synthesis and characterization of poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) nanoparticles for sustained bortezomib release using supercritical CO2 assisted particle formation combined with electrodeposition

Carbon dioxide assisted particle formation combined with electrospraying using supercritical CO2 (scCO2) as an aid (Carbon Dioxide Assisted Nebulization-Electrodeposition, CAN-ED) was used to produce Bortezomib loaded poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) P(3HB-co-3HHx) nanoparticles for sustained release. The morphology and structure of the prepared nanoparticles were investigated by SEM, TEM and FT-IR spectroscopy. Average diameter of particles obtained was 155 nm and the average core sizes of P(3HB-co-3HHx) nanoparticles were between 6 and 13 nm. The drug loading capacity, drug release and stability of Bortezomib loaded P(3HB-co-3HHx) nanoparticles were analyzed. The maximum loading capacity was achieved at pH = 6.0 in phosphate buffer (K2HPO4/KH2PO4). It was found that temperature did not affect the stability of Bortezomib loaded nanoparticles and it was good both at 37 °C and 4 °C. This study pointed out that CAN-ED is a green method to produce P(3HB-co-3HHx) nanoparticles for pH responsive targeting of Bortezomib especially to parts of the body where size exclusion is not crucial.