Hypophosphorous acid cross-linked layer-by-layer assembly of green polyelectrolytes on polyester-cotton blend fabrics for durable flame-retardant treatment
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
شیمی
شیمی آلی
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Hypophosphorous acid cross-linked layer-by-layer assembly of green polyelectrolytes on polyester-cotton blend fabrics for durable flame-retardant treatment Hypophosphorous acid cross-linked layer-by-layer assembly of green polyelectrolytes on polyester-cotton blend fabrics for durable flame-retardant treatment](/preview/png/8942919.png)
چکیده انگلیسی
In this work, a facile method to manufacture the layer-by-layer (LbL) assembled coating with durable flame-resistant effect on the polyester-cotton blend fabrics was reported. The LbL coating modified polyester-cotton fabric was treated with positively charged polyethyleneimine (PEI) and negatively charged oxidized sodium alginate (OSA) successively. Subsequently, the PEI/OSA coating was cross-linked by hypophosphorous acid (HA). As characterized by X-ray photoelectron spectroscopy and scanning electron microscopy, the HA cross-linked PEI/OSA coatings were successfully deposited on the surfaces of polyester and cotton fibers. Effects of the as-prepared coating on thermal stability, flame retardancy and laundering durability of the polyester-cotton blend fabrics were investigated. Thermogravimetric analysis revealed that the thermal decomposition of modified polyester-cotton fabric could be retarded obviously compared with the untreated one, as evidenced by the improvement in the 5% mass loss temperature by 30â°C. In the horizontal burning test, self-extinguishing behavior could be achieved for the polyester-cotton fabric treated with 5 bilayers coating. Moreover, the 77% and 75% reduction in the peak heat release rate and total heat release were observed for the polyester-cotton fabric treated with 10 bilayers coating. The treated fabrics still showed good flame retardant performance after 12 laundering cycles.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Carbohydrate Polymers - Volume 201, 1 December 2018, Pages 1-8
Journal: Carbohydrate Polymers - Volume 201, 1 December 2018, Pages 1-8
نویسندگان
Ying Pan, Longxiang Liu, Xin Wang, Lei Song, Yuan Hu,