کد مقاله | کد نشریه | سال انتشار | مقاله انگلیسی | نسخه تمام متن |
---|---|---|---|---|
9559252 | 1381146 | 2005 | 8 صفحه PDF | دانلود رایگان |
عنوان انگلیسی مقاله ISI
Synthesis and properties of organosoluble polyimides based on 2,2â²-diphenoxy-4,4â²,5,5â²-biphenyltetracarboxylic dianhydride
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
شیمی
شیمی آلی
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Synthesis and properties of organosoluble polyimides based on 2,2â²-diphenoxy-4,4â²,5,5â²-biphenyltetracarboxylic dianhydride Synthesis and properties of organosoluble polyimides based on 2,2â²-diphenoxy-4,4â²,5,5â²-biphenyltetracarboxylic dianhydride](/preview/png/9559252.png)
چکیده انگلیسی
A novel method for the preparation of 2,2â²-diphenoxy-4,4â²,5,5â²-biphenyltetracarboxylic dianhydride have been investigated. This new dianhydride contains flexible phenoxy side chain and a twist biphenyl moiety and it was synthesized by the nitration of an N-methyl protected 3,3â²,4,4â²-biphenyltetracarboxylic dianhydride and subsequent aromatic nucleophilic substitution with phenoxide. The overall yield was up to 75%. The dianhydride was polymerized with five different aromatic diamines to afford a series of aromatic polyimides. The polyimide properties such as inherent viscosity, solubility, UV transparency and thermaloxidative properties were investigated to illustrate the contribution of the introduction of phenoxy group at 2- and 2â²-position of BPDA dianhydride. The resulting polyimides possessed excellent solubility in the fact that the polyimide containing rigid diamines such as 1,4-phenylenediamine and 4,4â²-oxydianiline were soluble in various solvents such as N-methyl-2-pyrrolidone, N,N-dimethylacetamide, dimethyl sulfoxide and chloroform. The glass-transition temperatures of the polymers were in the range of 255-283 °C. These polymers exhibited good thermal stability with the temperatures at 5% weight loss range from 470 to 528 °C in nitrogen and 451 to 521 °C in air, respectively. The polyimide films were found to be transparent, flexible, and tough. The films had a tensile strength, elongation at break, and Young's modulus in the ranges 105-168 MPa, 15-51%, 1.87-2.38 GPa, respectively.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Polymer - Volume 46, Issue 5, 14 February 2005, Pages 1693-1700
Journal: Polymer - Volume 46, Issue 5, 14 February 2005, Pages 1693-1700
نویسندگان
Zhiming Qiu, Suobo Zhang,