Poly(ethylene oxide)/Laponite nanocomposites via melt-compounding: effect of clay modification and matrix molar mass

The nanocomposites based on the pure Laponite clay as well as the modified clays display an intercalated structure with a modest intergallery spacing. The ion-dipole modification with the PEG's was ineffective in improving the compatibility between PEO and the Laponite silicate layers. Their respective mechanical properties were found to be increased a little, which can be attributed to the low effective aspect ratio of the silicate platelets present in the nanocomposites. This is caused by the low initial aspect ratio of Laponite (w/t=25) and the limited basal spacing increase. The addition of clay does not result in nucleation of the PEO crystallisation. In contrast, the crystallisation was inhibited, resulting in decreased heat of fusions, especially for the pure Laponite nanocomposites. The nanocomposites based on the modified Laponites display a good thermal stability.