Post-annealing effects on shallow-junction characteristics caused by 20Â keV BGe molecular ion implantation
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سطوح، پوششها و فیلمها
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Post-annealing effects on shallow-junction characteristics caused by 20Â keV BGe molecular ion implantation Post-annealing effects on shallow-junction characteristics caused by 20Â keV BGe molecular ion implantation](/preview/png/9817767.png)
چکیده انگلیسی
This study examines the post-annealing-dependent behaviors of the shallow junction produced by implanting 1015 cmâ2 20 keV BGe ions into n-type ã1 0 0ã silicon specimens. Post-annealing treatments consisted of one- and two-step annealing including both furnace annealing (FA) and rapid thermal annealing (RTA). Comparison of the one-step FA at 550 °C and the one-step RTA at 1050 °C revealed that boron depth profiles were slightly diffused in the former but exhibited considerable transient-enhanced diffusion (TED) in the latter. However, both the one-step FA- and RTA-annealed germanium depth profiles barely diffused, while the latter diffusing slightly deeper than the former. The optimum value of junction depth (xj) times sheet resistance (Rs) was obtained with one-step FA at 550 °C for 1 h. The two-step annealing (FA at 550 °C and RTA at 1050 °C) results showed that the RTA-induced TED in the boron depth profiles could be effectively retarded only when FA took place for more than 3 h. Again, germanium depth profiles are also barely diffused while the corresponding TEDs were larger than those in one-step FA but smaller than those in one-step RTA. Furthermore, the two-step annealing of FA at 550 °C for 3 h followed by RTA at 1050 °C for 30 s is suggested when attempting to obtain an optimum value of xjRs.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Nuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms - Volume 237, Issues 1â2, August 2005, Pages 312-317
Journal: Nuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms - Volume 237, Issues 1â2, August 2005, Pages 312-317
نویسندگان
J.H. Liang, Y.J. Sang, C.-H. Wang, T.W. Wang, J.Y. Hsu, H. Niu, M.S. Tseng,