Single crystal Tl0.3MoO3 growth by electrolytic reduction method of a Tl2CO3-MoO3 melts
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
فیزیک و نجوم
فیزیک ماده چگال
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
Single crystals of quasi-one-dimensional charge-density-wave conductor blue bronze Tl0.3MoO3 have been grown by electrolytic reduction method using the raw materials Tl2CO3-MoO3 with composition around 1:4.3 mol ration. The electrolytic temperature was about 570 °C, and electrolytic current was 25 mA during the electrolytic process. By this method, the Tl0.3MoO3 single crystals obtained have a relatively large average size and high quality. Platelet crystals with typical dimensions of 7Ã2Ã1 mm3 were obtained. The crystal structure is monoclinic with space group C2/m. The parameters of the unit cell of the single crystal are as follows: a=18.486(6) Ã
, b=7.555(2)Â Ã
, c=10.032(3)Â Ã
and β=118.38(3)°. The C-center symmetry of Tl0.3MoO3 crystal is demonstrated by the selected area electron diffraction (SAED) patterns in the transmission electron microscope (TEM). The full-width at half-maximum (FWHM) of the rocking curve of the (201¯) Bragg peak of the Tl0.3MoO3 was approximately 0.4°. These are evidences that the single crystal is of high quality. The temperature dependence of the resistivity shows that a metal-semiconductor transition occurs near 181 K.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Crystal Growth - Volume 285, Issues 1â2, 15 November 2005, Pages 81-87
Journal: Journal of Crystal Growth - Volume 285, Issues 1â2, 15 November 2005, Pages 81-87
نویسندگان
Changzhen Li, Rui Xiong, Di Yin, Zheng Tang, Junfeng Wang, Dahua Li, Zuxing Yu, Jing Shi,