Specific heat of TbMn2(H,D)2

Specific heat (SH) measurements on TbMn2(H,D)2 powders have been performed in the temperature range from 2 to 350 K, in zero magnetic field and in 9 T. Due to the low heat conductivity of the samples, the measurements were carried out on a mixed Cu- and sample-powder pellet. For TbMn2, the anti-ferromagnetic phase transition was manifest by a single SH peak at TN=47 K, whereas a double SH peak at 281 and 288 K and an upturn below 5 K were observed for the hydride sample. Upon applying the magnetic field of 9 T, the SH upturn was suppressed, whereas no visible influence was found on the specific heat in the whole temperature range above 10 K as well as on the double peak.