Effect of the Cu/Ba ratio for the YBCO deposition onto IBAD template by the MOCVD method

YBa2Cu3O7−x (YBCO) thin films were fabricated by the metal organic chemical vapor deposition (MOCVD) using a single liquid source. The copper/barium (Cu/Ba) ratio was varied from 1.26 to 1.38 to optimize the deposition condition. The IBAD template (CeO2/YSZ/stainless steel) was used as a substrate. The growth features of the YBCO films were not significantly influenced by the Cu/Ba ratio, while the superconducting transition temperature (Tc) and critical current (Ic) depended on the Cu/Ba ratio. When Cu/Ba ratio was between 1.26 and 1.29, Tc was as low as 80 K, while as Cu/Ba ratio increased to 1.38, it increased to above 85 K. The highest Tc (89.0 K) and Ic (46.3 A/cm-width) were achieved at the Cu/Ba ratio of 1.38 (Y:Ba:Cu = 1:2.1:2.9). It indicates that the optimum Cu/Ba ratio which differs from stoichiometric balance exists for the formation of the superconducting phase with a high Tc and Ic in MOCVD method.