A novel oligomer containing DOPO and ferrocene groups: Synthesis, characterization, and its application in fire retardant epoxy resin
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
شیمی
شیمی آلی
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
A novel oligomer (PFDCHQ) based on 9,10-dihydro-9-oxa-10-phosphaphenanthrene â10-oxide (DOPO) and ferrocene groups was synthesized successfully, aiming at improving the flame retardant efficiency of diglycidyl ether of bisphenol A epoxy resin (DGEBA). FTIR, 1H NMR and 31P NMR were used to confirm the chemical structure of PFDCHQ. The high char yields of 60.3â¯wt% and 20.1â¯wt% were obtained for PFDCHQ from TGA results in nitrogen and air atmosphere, respectively. The thermal degradation mechanism of PFDCHQ was investigated by TG-FTIR and Py-GC/MS. The limiting oxygen index (LOI) of EP-5 with 5â¯wt% loading of PFDCHQ increased to 32.0% and the UL-94 V-0 rating was achieved, showing a notable blowing-out effect. In contrast to EP-0, the peak of the heat release rate (pHRR) and total heat release (THR) of EP-5 decreased by 18.0% and 10.3%. The flame retardant mechanism of PFDCHQ in epoxy resin was studied by TG-FTIR, SEM and Raman. SEM and Raman results indicated the formation of coherent and dense char residue with high degree of graphitization due to the incorporation of PFDCHQ. In UL-94, the blowing-out effect dominantly accounted for the enhanced flame retardancy in combination with optimized char structure. Furthermore, the addition of PFDCHQ improved the Young's modulus compared to EP-0.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Polymer Degradation and Stability - Volume 156, October 2018, Pages 111-124
Journal: Polymer Degradation and Stability - Volume 156, October 2018, Pages 111-124
نویسندگان
Yi Wen, Zhou Cheng, Wenxiong Li, Zhi Li, Duijun Liao, Xiaoping Hu, Ning Pan, Deyi Wang, T. Richard Hull,