Effect of diffusible hydrogen content on embrittlement of P92 steel
Keywords: حرارت منطقه آسیب دیده است; Implant test; Diffusible hydrogen; Lower critical stress; P92 steel; Hydrogen assisted cracking; Heat affected zone;