Failure analysis of a weld-decayed austenitic stainless steel

► We document a failure analysis on weld decay in stainless steel due to sensitisation.
► It is less likely that hydrogen affected the failure.
► The electropolishing process could not cause hydrogen embrittlement.
► Recommend introducing coincidence site lattice boundaries for preventing the failure.