Electrospun poly (butylene succinate)/cellulose nanocrystals bio-nanocomposite scaffolds for tissue engineering: Preparation, characterization and in vitro evaluation
ترجمه فارسی عنوان
الکترو پون پلاستیک (بوتیلن سوکسینات) / نانوکریستولهای سلولز داربستهای زیستی نانو کامپوزیت برای مهندسی بافت: تهیه، مشخص کردن و ارزیابی درون آزمایشگاهی
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
شیمی
شیمی آلی
چکیده انگلیسی
Three-dimensional (3D) bio-nanocomposite poly (butylene succinate) (PBS)/cellulose nanocrystals (CNC) scaffolds were fabricated by a solvent mixture of chloroform (CF) and methanol (MeOH) via electrospinning technique. Morphological, thermal, mechanical, and hydrophilicity as well as in vitro degradation and biocompatibility properties of the electrospun fibrous bio-nanocomposite scaffolds were investigated. Scanning electron microscopy (SEM) indicated that the average diameter of the electrospun fibers decreased with increase in CNC concentration. The incorporation of CNC not only enhanced the thermostability, and 0.5â¯wt% and 1â¯wt% CNC significantly increased the crystallinity of PBS matrix, but also improved the tensile strength, Young's modulus and hydrophilicity of PBS matrix with an optimum 3â¯wt% CNC. Moreover, it also improved the porosity and decreased the density of the PBS/CNC scaffolds. In vitro degradation results showed that PBS/CNC3 scaffold had better bio-degradation ability, from 4.5% of neat PBS to 13.74% of PBS/CNC3 in 28 days. 3T3 fibroblast cell culture was performed to confirm the good biocompatibility of the scaffolds. Cells were found to proliferate better on the PBS/CNC3 scaffolds, as compared to neat PBS scaffolds in 7 days.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Polymer Testing - Volume 71, October 2018, Pages 101-109
Journal: Polymer Testing - Volume 71, October 2018, Pages 101-109
نویسندگان
An Huang, Xiangfang Peng, Lihong Geng, Lingli Zhang, Keqing Huang, Binyi Chen, Zhipeng Gu, Tairong Kuang,