Statistical analysis of high cycle fatigue life and inclusion size distribution in shot peened 300M steel
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
σsCI95GEVFGAHRCCRSHCFXmaxCDFeCCIEDSVHCFFine granular areaVacuum arc remeltingStatistics of extreme valuesGeneralized Extreme Value - ارزش افراطی عمومیultimate tensile strength - استحکام کششی نهاییSurface residual stress - استرس باقی مانده سطحیCompressive residual stress - استرس باقی مانده فشاریCumulative Distribution Function - تابع توزیع تجمعیProbability density function - تابع چگالی احتمالStatistical analysis - تحلیل آماریElectron channeling contrast imaging - تصویربرداری کنتراست کنترلی الکترونیarea - حوزهFatigue - خستگیHigh Cycle Fatigue - خستگی چرخه بالاVery high cycle fatigue - خستگی چرخه بسیار زیادstandard error - خطای استانداردRSM - روششناسی سطح پاسخshot peening - ساچمه زنیcoefficient of determination - ضریب تعیینLongitudinal - طولیenergy dispersive spectroscopy - طیف سنجی پراکنده انرژیconfidence interval - فاصله اطمینانHigh strength steel - فولاد با مقاومت بالاSEM - مدل معادلات ساختاری / میکروسکوپ الکترونی روبشیYoung’s modulus - مدول یانگscanning electron microscope - میکروسکوپ الکترونی اسکنStress ratio - نسبت استرسPoisson’s ratio - نسبت پواسونInclusion - ورودwt.% - وزن٪Shape parameter - پارامتر شکلScale parameter - پارامتر مقیاسLocation parameter - پارامتر مکانX-ray diffraction - پراش اشعه ایکسXRD - پراش اشعه ایکسPdf - پی دی افSeV - چطوریVAR - که در آن
موضوعات مرتبط
مهندسی و علوم پایه
سایر رشته های مهندسی
مهندسی مکانیک
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
In order to fully exploit the benefits of shot peening process in terms of fatigue performance, the proper choice of peening conditions is indispensable, which is largely material specific. In this study, the influence of 3 different peening conditions on the axial fatigue life of high strength 300M steel (modified AISI 4340) was investigated in the high cycle fatigue regime. A statistical estimate of 90% survival life at 95% confidence interval was made to rigorously compare the fatigue performance of the material with different surface conditions. The peening induced roughness, compressive residual stresses and their relaxation during cyclic loading were quantified. It was however revealed, that shot peening had no significant effect on this material when tested at 55% of yield strength (Ïy,0.2). The fatigue life was dominated by the larger non-metallic inclusions within the bulk material. An empirical relationship between inclusion size and fatigue life was proposed based on this observation. Furthermore, the inclusion size distribution was well described using Gumbel extreme value distribution allowing the largest inclusion to be predicted in a given volume of steel. The prediction results were in good agreement with the experimentally observed value of the largest inclusion size observed at a fatigue crack initiation site.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: International Journal of Fatigue - Volume 118, January 2019, Pages 126-138
Journal: International Journal of Fatigue - Volume 118, January 2019, Pages 126-138
نویسندگان
Amrita Bag, Dorian Delbergue, Philippe Bocher, Martin Lévesque, Myriam Brochu,