![عکس صفحه اول مقاله: Biodegradable CaMgZn bulk metallic glass for potential skeletal application Biodegradable CaMgZn bulk metallic glass for potential skeletal application](/preview/png/1022.png)
A low density and high strength alloy, Ca65Mg15Zn20 bulk metallic glass (CaMgZn BMG), was evaluated by both in vitro tests on ion release and cytotoxicity and in vivo implantation, aimed at exploring the feasibility of this new biodegradable metallic material for potential skeletal applications. MTT assay results showed that the experimental CaMgZn BMG extracts had no detectable cytotoxic effects on L929, VSMC and ECV304 cells over a wide range of concentrations (0–50%), whereas for MG63 cells concentrations in the range ∼5–20% promoted cell viability. Meanwhile, alkaline phosphatase (ALP) activity results showed that CaMgZn BMG extracts increased alkaline phosphatase (ALP) production by MG63 cells. However, Annexin V–fluorescein isothiocyanate and propidium iodide staining indicated that higher concentrations (50%) might induce cell apoptosis. The fluorescence observation of F-actin and nuclei in MG63 cells showed that cells incubated with lower concentrations (0–50%) displayed no significant change in morphology compared with a negative control. Tumor necrosis factor-α expression by Raw264.7 cells in the presence of CaMgZn BMG extract was significantly lower than that of the positive and negative controls. Animal tests proved that there was no obvious inflammation reaction at the implantation site and CaMgZn BMG implants did not result in animal death. The cortical thickness around the CaMgZn BMG implant increased gradually from 1 to 4 weeks, as measured by in vivo micro-computer tomography.
Journal: Acta Biomaterialia - Volume 7, Issue 8, August 2011, Pages 3196–3208