Mechanical, barrier and morphological properties of pea starch and peanut protein isolate blend films

Mechanical, barrier and morphological properties of edible films based on blends of Pea starch (PS) and Peanut protein isolate (PPI) plasticized with glycerol (30%, w/w) were investigated. As PPI ratio in PS/PPI blends increased, the thickness of films decreased, the opacity slightly elevated and color intensified. The addition of PPI to the PS film significantly reduced tensile strength from 5.44 MPa to 3.06 MPa, but increased elongation from 28.56% to 98.12% with the incorporation of PPI into PS at 50% level. Film solubility value fell from 22.31% to 9.78% upon the incorporation of PPI ranged from 0 to 50% level. When PPI was added into PS film at 40% level, the WVP and WVTR of the films markedly dropped from 11.18% to 4.19% and 6.16 to 1.95%, respectively. Scanning electron microscopy (SEM) of the surface of films showed that many swollen starch granules were presented in the 100% PS film, while 100% PPI film was observed to have rougher surfaces with presence of pores or cavities. The PS/PPI blend films upon the incorporation of PPI at 20% and 50% level were not homogeneous. However, the smoother film surface was observed in PS/PPI blend films with the addition of PPI at 40% level. SEM image of the cross-sections of the films revealed that the 100% PS film showed a uniform and compact matrix without disruption, and pore formation and 100% PPI film displayed a smooth structure. Rougher and flexible network was shown in blend film with the addition of PPI reaching 40% level.