Cyclopolymerization XXXIII. Radical polymerizations and copolymerizations of 1,6-dienes with 2-phenylallyl group and thermal properties of polymers derived therefrom

Radical polymerizations of α-allyloxymethylstyrene (1) and copolymerizations of α-(2-phenylallyloxy)methylstyrene (2) were undertaken to acquire comprehensive understanding on polymerization behavior of these dienes and to get polymers with high thermal stability and high glass transition temperature (Tg). One of the monofunctional counterparts of 1 is a derivative of α-methylstyrene, the ceiling temperature of which is low, and the other is an allyl compound that is well-known for the low homopolymerization tendency. This means that the intermolecular propagation reactions leading to pendant uncyclized units are suppressed during the polymerization of 1 to yield highly cyclized polymers. In fact, the degree of cyclization of poly(1) obtained at 140 °C attained the value 92%. Structural studies revealed that repeat cyclic units of poly(1) consist exclusively of five-membered rings. Poly(1) was found to be stable up to 300 °C, but its Tg values were detected at around 100 °C. They are considerably lower than the targeted values which should lie between 180 and 220 °C. An additional drawback of poly(1) is its low molecular weight probably due to a degradative chain transfer. For this reason, copolymerizations of 2 with 1 and with styrene were also carried out to seek for the possibility to control the thermal properties precisely. Monomer 2 was chosen, since it has been reported in our previous work that it yields polymers with thermal stability up to 300 °C and Tg higher than 250 °C. Copolymerization of 2 with styrene afforded polymers with desired thermal properties and high molecular weight.